Quantitative characterization of physico-chemical properties of the active layers of reverse osmosis and nanofiltration membranes, and their relation to membrane performance

The main objectives of this dissertation were: (i) to develop experimental and analytical procedures to quantify different physico-chemical properties of the ultra-thin (~ 100 nm) active layers of reverse osmosis (RO) and nanofiltration (NF) membranes and their interactions with contaminants; (ii) to use such procedures to evaluate the similarities and differences between the active layers of different RO/NF membranes; and (iii) to relate characterization results to membrane performance. Such objectives were motivated by the current limited understanding of the physico-chemical properties of active layers as a result of traditional characterization techniques having limitations associated with the nanometer-scale spatial resolution required to study these ultra-thin films. Functional groups were chosen as the main active layer property of interest. Specific accomplishments of this study include the development of procedures to quantify in active layers as a function of pH: (1) the concentration of both negatively and positively ionized functional groups; (2) the stoichiometry of association between ions (i.e., barium) and ionized functional groups (i.e., carboxylate and sulfonate); and (3) the steric effects experienced by ions (i.e., barium). Conceptual and mathematical models were developed to describe experimental results. The depth heterogeneity of the active layer physico-chemical properties and interactions with contaminants studied in this dissertation was also characterized. Additionally, measured concentrations of ionized functional groups in the polyamide active layers of several commercial RO/NF membranes were used as input in a simplified RO/NF transport model to predict the rejection of a strong electrolyte (i.e., potassium iodide) and a weak acid (i.e., arsenious acid) at different pH values based on rejection results at one pH condition. The good agreement between predicted and experimental results showed that the characterization procedures developed in this study serve as useful tools in the advancement of the understanding of the properties and structure of the active layers of RO/NF membranes, and the mechanisms of contaminant transport through them.

Development of polymeric drug delivery vehicles for targeted cancer therapy

The aim of my Ph. D. thesis is to generalize a method for targeted anti-cancer drug delivery. Hydrophilic polymer-drug conjugates involve complicated synthesis; drug-encapsulated polymeric nanoparticles limit the loading capability of payloads. This thesis introduces the concept of nanoconjugates to overcome difficulties in synthesis and formulation. Drugs with hydroxyl group are able to initiate polyester synthesis in a regio- and chemo- selective way, with the mediation of ligand-tunable Zinc catalyst. Herein, three anti-cancer drugs are presented to demonstrate the high efficiency and selectivity in the method (Chapter 2-4). The obtained particles are stable in salt solution, releasing drugs over weeks in controlled manner. With the conjugation of aptamer, particles are capable to target prostate cancer cells in vitro. These results open the gateway to evaluate the in vivo efficacy of nanoconjugates for target cancer therapy (Chapter 5). Mechanism study of the polymerization leads to the discovery of chemosite selective synthesis of prodrugs with acrylate functional groups. Functional copolymer-drug conjugates will expand the scope of nanoconjugates (Chapter 6). Liposome-aptamer targeting drug delivery vehicle is well studied to achieve reversible cell-specific delivery of non-hydoxyl drugs e.g. cisplatin (Chapter 7). New monomers and polymerization mechanisms are explored for polyester in order to synthesize nanoconjugates with variety on properties (Chapter 8). Initial efforts to apply this type of prodrugs will be focused on the preparation of hydrogels for stem cell research (Chapter 9).

Synthesis and structural stability of metal-organic frameworks

Metal-organic frameworks (MOFs) have attracted significant attention during the past decade due to their high porosity, tunable structures, and controllable surface functionalities. Therefore many applications have been proposed for MOFs. All of them however are still in their infancy stage and have not yet been brought into the market place. In this thesis, the background of the MOF area is first briefly introduced. The main components and the motifs of designing MOFs are summarized, followed by their synthesis and postsynthetic modification methods. Several promising application areas of MOFs including gas storage and separation, catalysis and sensing are reviewed. The current status of commercialization of MOFs as new chemical products is also summarized. Examples of the design and synthesis of two new MOF structures Eu(4,4′,4′′,4′′′-(porphine-5,10,15,20-tetrayl)tetrakis(benzoic acid))·2H2O∙xDMF and Zn4O(azobenzene-4,4’-dicarboxylic acid)3∙xNMP are described. The first one contains free-base porphyrin centers and the second one has azobenzene components. Although the structures were synthesized as designed, unfortunately they did not possess the expected properties. The research idea to use MOFs as template materials to synthesize porous polymers is introduced. Several methods are discussed to grow PMMA into IRMOF-1 (Zn4O(benzene-1,4-dicarboxylate)3, IR stands for isoreticular) structure. High concentration of the monomers resulted in PMMA shell after MOF digestion while with low concentration of monomers no PMMA was left after digestion due to the small iii molecular weight. During the study of this chapter, Kitagawa and co-workers published several papers on the same topic, so this part of the research was terminated thereafter. Many MOFs are reported to be unstable in air due to the water molecules in air which greatly limited their applications. By incorporating a number of water repelling functional groups such as trifluoromethoxy group and methyl groups in the frameworks, the water stability of MOFs are shown to be significantly enhanced. Several MOFs inculding Banasorb-22 (Zn4O(2-trifluoromethoxybenzene-1,4-dicarboxylate)3), Banasorb-24 (Zn4O(2, 5-dimethylbenzene-1,4-dicarboxylate)3) and Banasorb-30 (Zn4O(2-methylbenzene-1,4-dicarboxylate)3) were synthesized and proved to have isostructures with IRMOF-1. Banasorb-22 was stable in boiling water steam for one week and Banasorb-30’s shelf life was over 10 months under ambient condition. For comparison, IRMOF-1’s structure collapses in air after a few hours to several days. Although MOF is a very popular research area nowadays, only a few studies have been reported on the mechanical properties of MOFs. Many of MOF’s applications involve high pressure conditions, so it is important to understand the behavior of MOFs under elivated pressures. The mechanical properties of IRMOF-1 and a new MOF structure Eu2(C12N2O4H6)3(DEF)0.87(H2O)2.13 were studied using diamond anvil cells at Advanced Photon Source. IRMOF-1 experienced an irriversible phase transtion to a nonporous phase followed by amorphization under high pressure. Eu2(C12N2O4H6)3(DEF)0.87(H2O)2.13 showed reversible compression under pressure up to 9.08GPa.